Abstract

Resistance spot welds (RSWs) in advanced high strength steels frequently exhibit interfacial failure during cross-tension testing: a mode of fracture associated with low-energy absorption. Automotive assembly lines include a paint application and baking cycle after the vehicle assembly and joining processes to cure paint and any adhesives used for assembly. In this article, the effects of a typical baking cycle: 180 °C for 20 min, on the failure mode and energy absorption during cross-tension testing of RSWs made in a TRIP1180 steel are reported. Further, short-time baking cycles of 30 s, 90 s, and 4 min were employed to investigate how quickly these baking effects are activated. RSWs, which exhibited interfacial failure and a low-energy absorption of 30.9 J in the as-welded condition, saw a change in a failure mode to partial interfacial failure and a 260% increase in energy absorption after baking for 30 s. After baking for a longer time (4 min), welds failed by button pull-out and exhibited a 296% increase in energy absorption during cross-tension testing. Baking for the full 20 min resulted in no additional improvement than was observed in the 4 min condition. The mechanisms responsible for the majority of the improvement in weld performance during baking are found to be activated after only 30 s of baking.

References

1.
Lesch
,
C.
,
Kwiaton
,
N.
, and
Klose
,
F. B.
,
2017
, “
Advanced High Strength Steels (AHSS) for Automotive Applications—Tailored Properties by Smart Microstructural Adjustments
,”
Steel Res. Int.
,
88
(
10
), pp.
1
21
. 10.1002/srin.201700210
2.
Schmitt
,
J.
, and
Iung
,
T.
,
2018
, “
New Developments of Advanced High-Strength Steels for Automotive Applications
,”
C. R. Phys.
,
19
(
8
), pp.
641
656
. 10.1016/j.crhy.2018.11.004
3.
Rezaei Ashtiani
,
H. R.
, and
Zarandooz
,
R.
,
2015
, “
The Influence of Welding Parameters on the Nugget Formation of Resistance Spot Welding of Inconel 625 Sheets
,”
Metall. Mater. Trans. A
,
46
(
9
), pp.
4095
4105
. 10.1007/s11661-015-3030-1
4.
Marya
,
M.
, and
Gayden
,
X. Q.
,
2005
, “
Development of Requirements for Resistance Spot Welding Dual-Phase (DP600) Steels Part 1—The Causes of Interfacial Fracture
,”
Weld. Res.
,
84
(
11
), pp.
172s
182s
.
5.
Khan
,
M. I.
,
Kuntz
,
M. L.
, and
Zhou
,
Y.
,
2008
, “
Effects of Weld Microstructure on Static and Impact Performance of Resistance Spot Welded Joints in Advanced High Strength Steels
,”
Sci. Technol. Weld. Joining
,
13
(
3
), pp.
294
304
. 10.1179/174329308X271733
6.
Baltazar Hernandez
,
V. H.
,
Kuntz
,
M. L.
,
Khan
,
M. I.
, and
Zhou
,
Y.
,
2008
, “
Influence of Microstructure and Weld Size on the Mechanical Behavior of Dissimilar AHSS Resistance Spot Welds
,”
Sci. Technol. Weld. Joining
,
13
(
8
), pp.
769
776
. 10.1179/136217108X325470
7.
Pouranvari
,
M.
,
Marashi
,
S. P. H.
, and
Mousavizadeh
,
S. M.
,
2010
, “
Failure Mode Transition and Mechanical Properties of Similar and Dissimilar Resistance Spot Welds of DP600 and Low Carbon Steels
,”
Sci. Technol. Weld. Joining
,
15
(
7
), pp.
625
631
. 10.1179/136217110X12813393169534
8.
Marya
,
M.
,
Wang
,
K.
,
Hector
,
L. G.
, and
Gayden
,
X.
,
2006
, “
Tensile-Shear Forces and Fracture Modes in Single and Multiple Weld Specimens in Dual-Phase Steels
,”
ASME J. Manuf. Sci. Eng.
,
128
(
1
), pp.
287
298
. 10.1115/1.2137751
9.
Ghassemi-Armaki
,
H.
,
Kaczynski
,
C.
,
Benlatreche
,
Y.
,
Gibot
,
A.
, and
Dupuy
,
T.
,
2018
, “
Improvement of Weld Strength and Toughness After Paint Baking in Gen. 3 AHSS
,”
Metall. Mater. Trans. A
,
49
(
12
), pp.
6185
6196
.
10.
Smith
,
S.
,
Okada
,
T.
,
den Uijl
,
N. J.
,
van der Veldt
,
T.
,
Uchihara
,
M.
, and
Fukui
,
K.
,
2009
, “
Influence of the Paint Baking Cycle on the Mechanical Properties of AHSS Welded Structures in Automotive Assemblies
,”
International Automotive Body Congress (IABC), Global Powertrain Congress (GPC)
,
Vaals, The Netherlands
,
June 1–15
.
11.
Eftekharimilani
,
P.
,
van der Aa
,
E. M.
,
Petrov
,
R.
,
Hermans
,
M. J. M.
, and
Richardson
,
I. M.
,
2018
, “
Understanding the Effect of a Paint Bake Cycle on the Microstructure–Mechanical Properties Relationship of a Resistance Spot Welded Advanced High Strength Steel
,”
Metall. Mater. Trans. A
,
49
(
12
), pp.
6185
6196
. 10.1007/s11661-018-4912-9
12.
Park
,
G.
,
Kim
,
K.
,
Uhm
,
S.
, and
Lee
,
C.
,
2019
, “
Remarkable Improvement in Resistance Spot Weldability of Medium-Mn TRIP Steel by Paint-Baking Heat Treatment
,”
Mater. Sci. Eng. A
,
766
(
24
), p.
138401
. 10.1016/j.msea.2019.138401
13.
Chabok
,
A.
,
2019
, “
Resistance Welding of Advanced High Strength Steels
,”
Ph.D. thesis
,
University of Groningen
,
Groningen, Netherlands
.
14.
Tumuluru
,
M.
,
2010
, “
Effects of Baking on the Structure and Properties of Resistance Spot Welds in 780 MPa Dual-Phase and TRIP Steels
,”
Weld. J.
,
89
, pp.
91
100
.
15.
Shamsujjoha
,
M.
,
Enloe
,
C. M.
,
Chuang
,
A. C.
,
Coryell
,
J. J.
, and
Ghassemi-Armaki
,
H.
,
2021
, “
Mechanisms of Paint Bake Response in Resistance Spot-Welded First and Third Generation AHSS
,”
Materiala
,
15
.
16.
Lu
,
S.
,
Ghassemi-Armaki
,
H.
, and
Lin
,
B.
,
2019
, “
Effect of Bake-Hardening on Base Metal and Post-Weld Properties of 3rd Generation AHSS
,”
Great Designs in Steel
,
Livonia, MI
,
May 15–16
.
17.
Choi
,
D.
,
Uhm
,
S.
,
Enloe
,
C.
,
Lee
,
H.
,
Kim
,
G.
, and
Horvath
,
C.
,
2017
, “
Liquid Metal Embrittlement of Resistance Spot Welded 1180TRIP Steel-Effects of Crack Geometry on Weld Mechanical Performance
,”
Materials Science & Technology
,
Pittsburgh, PA
,
Oct. 8–12
.
18.
Speich
,
G. R.
,
1969
, “
Tempering of Low-Carbon Martensite
,”
Trans. Metall. Soc. AIME
,
245
, pp.
1969
2563
.
19.
Speich
,
G. R.
, and
Leslie
,
W. C.
,
1972
, “
Tempering of Steel
,”
Metall. Trans.
,
3
(
5
), pp.
1043
1054
. 10.1007/BF02642436
20.
Krauss
,
G.
,
2005
,
Steels: Processing, Structure, and Performance
,
ASM International
,
Materials Park, OH
.
You do not currently have access to this content.