A team approach involving a turbine engine company (Rolls-Royce), its single-crystal casting facilities, and a superalloy developer and ingot manufacturer (Cannon-Muskegon), utilizing the concepts of simultaneous engineering, has been used to develop CMSX-4 alloy successfully for turbine blade applications. CMSX-4 alloy is a second-generation nickel-base single-crystal superalloy containing 3 percent (wt) rhenium (Re) and 70 percent volume fraction of the coherent γ′ precipitate strengthening phase. Its finely balanced composition offers an attractive range of properties for turbine airfoil applications. In particular the alloy’s combination of high strength in relation to creep-rupture, mechanical and thermal fatigue, good phase stability following extensive high temperature, stressed exposure and oxidation, hot corrosion and coating performance, are attractive for turbine engine applications where engine performance and turbine airfoil durability are of prime importance. The paper details the single-crystal casting process and heat treatment manufacturing development for turbine blades in CMSX-4 alloy. Competitive single-crystal casting yields are being achieved in production and extensive vacuum heat treatment experience confirms CMSX-4 alloy to have a practical production solution heat treat/homogenization “window.” The creep-rupture data-base on CMSX-4 alloy now includes 325 data points from 17 heats including 3630 kg (8000 lb) production size heats. An appreciable portion of this data was machined-from-blade (MFB) properties, which indicate turbine blade component capabilities based on single-crystal casting process, component configuration, and heat treatment. The use of hot isostatic pressing (HIP) has been shown to eliminate single-crystal casting micropores, which along with the essential absence of γ/γ′ eutectic phase, carbides, stable oxide, nitride and sulfide inclusions, results in remarkably high mechanical fatigue properties, with smooth and particularly notched specimens. The Re addition has been shown not only to benefit creep and mechanical fatigue strength (with and without HIP), but also bare oxidation, hot corrosion (sulfidation), and coating performance. The high level of balanced properties determined by extensive laboratory evaluation has been confirmed during engine testing of the Rolls-Royce Pegasus turbofan.

1.
Pickering, F. E., (GE), “Advances in Turbomachinery,” Cliff Garrett Award Lecture, Aerosp. Eng., Jan. 1986, pp. 30–35.
2.
Gell, M., Duhl, D. N., Giamei, A. F., (PWA), “The Development of Single Crystal Superalloy Turbine Blades,” 4th Int. Symp.,2 Sept.1980, pp. 205–214.
3.
Wukusick, C. S., [GE (AE)], “Directional Solidification Alloy Development,” NAVAIR Contr. N62269-78-C-0315, Final Report, 25 Aug. 1980.
4.
Holmes, J. W., et al. (MIT), O’Hara, K. S. [GE (AE)], “Thermal Fatigue Testing of Coated Monocrystallize Superalloys,” ASTM STP 942, Phil., 1988, pp. 672–691.
5.
Strangmen, T. E., et al. (Garrett), “Development of Exothermically Cast Single Crystal MAR M 247 and Derivative Alloys,” 4th Int. Symp. Sept. 1980, pp. 215–224.
6.
Goulette, M. J., Spilling, P. D., Arthey, R. P., (RR), “Cost Effective Single Crystals,” 5th Int. Symp.,2 Oct. 1984, pp. 167–176.
7.
Ford, D. A., Arthey, R. P., (RR), “Development of Single Crystal Alloys for Specific Engine Applications,” 5th Int. Symp.,2 Oct. 1984, pp. 115–124.
8.
Doner, M., Heckler, J. A., (Allison), “Effects of Section Thickness and Orientation on the Creep-Rupture Properties of Two Advanced Single Crystal Alloys,” Aerospace Tech. Conf., Long Beach, CA, Oct. 1985.
9.
Bachelet, E., and Lamanthe, G., (Snecma), Nat. Symp.—Single Crystal Superalloys, Viallard-de-Lans (France), 26–28 Feb. 1986.
10.
Yamazaki, M., et al. (NRIM), “Alloy Design for High Strength Nickel-Base Single Crystal Alloys,” 5th Int. Symp.,2 Oct. 1984, pp. 157–166.
11.
Petrov, D. A., and Tumanov, A. T., “The Use of Single Crystal Blades,” Aircraft Engineering, No. 9, 1973.
12.
Harris, K., Erickson, G. L., and Schwer, R. E.,(CM), “Development of the Single Crystal Alloys CMSX-2 and CMSX-3 for Advanced Technology Turbines,” ASME Paper No. 83-GT-244.
13.
Harris, K., Erickson, G. L., and Schwer, R. E., (CM), Verbal Presentation, TMS Mtg, Phil., PA, 3 Oct. 1983.
14.
Harris, K., Erickson, G. L., Schwer, R. E., (CM), “MAR M 247 Derivations—CM 247 LC DS Alloy, CMSX® Single Crystal Alloys, Properties and Performance,” 5th Int. Symp.,2 Oct. 1984, pp. 221–230.
15.
Harris, K., Erickson, G. L., Schwer, R. E., (CM), “CMSX® Single Crystal, CM DS and Integral Wheel Alloys—Properties and Performance,” Proc. Cost 50/501 Conf. Lie`e, Oct. 6–9, 1986, pp. 709–728.
16.
Wortmann, J., Wege, R., (MTU), Harris, K., Erickson, G. L., Schwer, R.E., (CM), “Low Density Single Crystal Superalloy CMSX-6®,” Proc. 7th World Conf. On Inv. Casting, Munich, 29 June 1988.
17.
Yukawa, N., et al. (Toyohashi Univ.), “High Performance Single Crystal Superalloys Developed by the d-Electrons Concept,” 6th Int. Symp.,2 Sept., 1988, pp. 225–234.
18.
Cetel, A. D., and Duhl, D. N., (PWA), “Second-Generation Nickel-Base Single Crystal Superalloy,” 6th Int. Symp.,2 Sept. 1988, pp. 235–244.
19.
Gell, M., Duhl, D. N., Gupta, K. K., and Sheffler, K. D., (PWA), JOM, July, 1987, pp. 11–15.
20.
Khan, T., (Onera), Brun, M., (Turbomeca), Symp. on Single Crystal Alloys, MTU/SMCT, Munich, June 1989.
21.
PWA Publication, “F100-PW-220, The Standard of Excellence,” June 1993.
22.
Wukusick, C. S., and Buchakjian, L., Jr. [GE(ARE)], “Improved Property-Balanced Nickel-Base Superalloys for Producing Single Crystal Articles,” U. K. Patent Application #GB 2 235 697 A, Mar. 13, 1991.
23.
Harris, K., Erickson, G. L., and Schwer, R. E., (CM), Frasier, D. J., Whetstone, J. R., (Allison), “Process and Alloy Optimization for CMSX-4 Superalloy Single Crystal Airfoils,” Proc. Cost Conf. Lie`e, Sept. 24–27, 1990, Part II, pp. 1281–1300.
24.
Harris, K., Erickson, G. L., Sikkenga, S. L., (CM), Brentnall, W. D., Aurrecoechea, J. M., and Kubarych, K. G., (Solar®), “Development of the Rhenium Containing Superalloys CMSX-4® and CM 186 LC® for Single Crystal Blade and Directionally Solidified Vane Applications in Advanced Turbine Engines,” 7th Int. Symp.,2 Sept. 1992, pp. 297–306.
25.
Kubarych, K. G., Aurrecoechea, J. M., (Solar®), “Post Field Test Evaluation of an Advanced Industrial Gas Turbine First Stage Turbine Blade,” TMS/ASM Materials Wk ’93 Proc., Pittsburgh, PA, 17–21 Oct 1993.
26.
Pratt, D. C., and Wilkinson, D. H., (AETC), 6th Wld. Conf. on Inv. Casting, Oct. 1984.
27.
Isobe, S., et al. (Daido), “The Effects of Impurities on Defects in Single Crystals of Nasair 100,” Proc. Int. Gas Turbine Conf., Tokyo, Oct. 1983.
28.
Harris, K., CM Report—“Status CMSX-4 Alloy,” 31 Oct. 1989.
29.
Harris, K., CM Report—“High Temperature Ageing Heat Treatment CMSX-4 Alloy,” 14 Dec. 1989.
30.
Giamei, A. F., and Anton, D. L., (UTRC), “Rhenium Additions to a Ni-Base Superalloy: Effects on Microstructure,” Met. Trans. A. 16A, pp. 1997–2005, Nov. 1985.
31.
Blavette, D., (Faculte´ des Sciences de Rouen), Caron, P., Khan, T., (Onera), Scripta Met., Vol. 20, No. 10, Oct. 1986.
32.
Blavette, D., (Faculte´ des Sciences de Rouen), Caron, P., Khan, T., (Onera), “An Atom-Probe Study of Some Fine Scale Microstructural Features in Ni-Base Single Crystal Superalloys,” 6th Int. Symp.,2 Sept. 1988, pp. 305–314.
33.
Meyer-Olbersleben, F., Re´zai-Aria, F., (Swiss Fed. Inst, of Technology), Goldschmidt, D., (MTU), “Investigation of the Thermal Fatigue Behaviour of Single Crystal Nickel-Based Superalloys SRR 99 and CMSX-4,” 7th Int. Symp.,2 Sept. 1992, pp. 785–794.
34.
U.S. Patent No. 4,935,072 (Garrett).
35.
Pessah, M., Caron, P., and Khan, T., (Onera), “Effect of μ Phase on the Mechanical Properties of a Nickel-Base Single Crystal Superalloy,” 7th Int. Symp.,2 Sept. 1992, pp. 567–576.
36.
Harris, K., Erickson, G. L., and Schwer, R. E., (CM), “Directionally Solidified and Single-Crystal Superalloys,” ASM International Metals Handbook, Vol. 1; Properties & Selection, pp. 1995–1006. 1989.
This content is only available via PDF.
You do not currently have access to this content.