1-4 of 4
Keywords: intergranular fracture
Close
Follow your search
Access your saved searches in your account

Would you like to receive an alert when new items match your search?
Close Modal
Sort by
Proceedings Papers

Proc. ASME. PVP2020, Volume 6: Materials and Fabrication, V006T06A010, August 3, 2020
Paper No: PVP2020-21239
... because of an intergranular fracture mechanism initiated at the carbides-rich interface. This mechanism was consistently observed for specimens with fatigue precrack fronts in the hard layer. To model the brittle behavior of the MA interface, the stress distributions on the MA interface were calculated...
Proceedings Papers

Proc. ASME. PVP2020, Volume 6: Materials and Fabrication, V006T06A083, August 3, 2020
Paper No: PVP2020-21021
...) with a concomitant increase in trap-site occupancy, implying that the trapped hydrogen controlled the hydrogen-induced IG fracture and ductility loss in pure Ni. hydrogen embrittlement pure nickel intergranular fracture segregation thermal desorption analysis secondary iron mass spectrometry...
Proceedings Papers

Proc. ASME. PVP2019, Volume 6B: Materials and Fabrication, V06BT06A030, July 14–19, 2019
Paper No: PVP2019-93477
... alloy compared to the pure Ni; (II) hydrogen transportation towards grain boundaries are required to cause the IG fracture in the Cu-Ni alloy. Keywords: hydrogen embrittlement, nickel, copper-nickel alloy, intergranular fracture, tensile tests 1. INTRODUCTION To achieve widespread acceptance of fuel...
Proceedings Papers

Proc. ASME. PVP2013, Volume 6A: Materials and Fabrication, V06AT06A009, July 14–18, 2013
Paper No: PVP2013-97618
... found that in the case of uniaxial stretch continuous failure elements appeared on the grain boundary perpendicular to the stretching direction, closest to the loading surface. This led to the formation of the so-called intergranular fracture ‘crack’. The simulation results showed that as the uniaxial...