Mechanical Response of Hollow Metallic Nanolattices: Combining Structural and Material Size Effects

[+] Author and Article Information
L. C. Montemayor

Division of Engineering and Applied Science,
California Institute of Technology,
Pasadena, CA 91125

J. R. Greer

Division of Engineering and Applied Science,
California Institute of Technology,
Pasadena, CA 91125
e-mail: jrgreer@caltech.edu

Contributed by the Applied Mechanics Division of ASME for publication in the JOURNAL OF APPLIED MECHANICS. Manuscript received November 20, 2014; final manuscript received April 9, 2015; published online June 3, 2015. Assoc. Editor: A. Amine Benzerga.

J. Appl. Mech 82(7), 071012 (Jul 01, 2015) (10 pages) Paper No: JAM-14-1531; doi: 10.1115/1.4030361 History: Received November 20, 2014; Revised April 09, 2015; Online June 03, 2015

Ordered cellular solids have higher compressive yield strength and stiffness compared to stochastic foams. The mechanical properties of cellular solids depend on their relative density and follow structural scaling laws. These scaling laws assume the mechanical properties of the constituent materials, like modulus and yield strength, to be constant and dictate that equivalent-density cellular solids made from the same material should have identical mechanical properties. We present the fabrication and mechanical properties of three-dimensional hollow gold nanolattices whose compressive responses demonstrate that strength and stiffness vary as a function of geometry and tube wall thickness. All nanolattices had octahedron geometry, a constant relative density, ρ ∼ 5%, a unit cell size of 5–20 μm, and a constant grain size in the Au film of 25–50 nm. Structural effects were explored by increasing the unit cell angle from 30 deg to 60 deg while keeping all other parameters constant; material size effects were probed by varying the tube wall thickness, t, from 200 nm to 635 nm, at a constant relative density and grain size. In situ uniaxial compression experiments revealed an order of magnitude increase in yield stress and modulus in nanolattices with greater lattice angles, and a 150% increase in the yield strength without a concomitant change in modulus in thicker-walled nanolattices for fixed lattice angles. These results imply that independent control of structural and material size effects enables tunability of mechanical properties of three-dimensional architected metamaterials and highlight the importance of material, geometric, and microstructural effects in small-scale mechanics.

Copyright © 2015 by ASME
Your Session has timed out. Please sign back in to continue.


Fleck, N. A., Deshpande, V. S., and Ashby, M. F., 2010, “Micro-Architectured Materials: Past, Present and Future,” Proc. R. Soc. A, 466(2121), pp. 2495–2516. [CrossRef]
Gibson, L. J., and Ashby, M. F., 1999, Cellular Solids: Structure and Properties, Cambridge University Press, Cambridge, UK.
Wallach, J. C., and Gibson, L. J., 2001, “Mechanical Behavior of a Three-Dimensional Truss Material,” Int. J. Solids Struct., 38(40–41), pp. 7181–7196. [CrossRef]
Deshpande, V., and Fleck, N., 2001, “Collapse of Truss Core Sandwich Beams in 3-Point Bending,” Int. J. Solids Struct., 38(36–37), pp. 6275–6305. [CrossRef]
Deshpande, V. S., Fleck, N. A., and Ashby, M. F., 2001, “Effective Properties of the Octet-Truss Lattice Material,” J. Mech. Phys. Solids, 49(8), pp. 1747–1769. [CrossRef]
Zheng, X., Lee, H., Weisgraber, T. H., Shusteff, M., DeOtte, J., Duoss, E. B., Kuntz, J. D., Biener, M. M., Ge, Q., Jackson, J. A., Kucheyev, S. O., Fang, N. X., and Spadaccini, C. M., 2014, “Ultralight, Ultrastiff Mechanical Metamaterials,” Science, 344(6190), pp. 1373–1377. [CrossRef] [PubMed]
Meza, L. R., Das, S., and Greer, J. R., 2014, “Strong, Lightweight, and Recoverable Three-Dimensional Ceramic Nanolattices,” Science, 345(6202), pp. 1322–1326. [CrossRef] [PubMed]
Jang, D., Meza, L., Greer, F., and Greer, J., 2013, “Fabrication and Deformation of Three-Dimensional Hollow Ceramic Nanostructures,” Nat. Mater., 12, pp. 893–898. [CrossRef] [PubMed]
Valdevit, L., Godfrey, S. W., Schaedler, T. A., Jacobsen, A. J., and Carter, W. B., 2013, “Compressive Strength of Hollow Microlattices: Experimental Characterization, Modeling, and Optimal Design,” J. Mater. Res., 28(17), pp. 2461–2473. [CrossRef]
Torrents, A., Schaedler, T. A., Jacobsen, A. J., Carter, W. B., and Valdevit, L., 2012, “Characterization of Nickel-Based Microlattice Materials With Structural Hierarchy From the Nanometer to the Millimeter Scale,” Acta Mater., 60(8), pp. 3511–3523. [CrossRef]
Schaedler, T. A., Jacobsen, A. J., Torrents, A., Sorensen, A. E., Lian, J., Greer, J. R., Valdevit, L., and Carter, W. B., 2011, “Ultralight Metallic Microlattices,” Science, 334(6058), pp. 962–965. [CrossRef] [PubMed]
Ng, K. Y., Lin, Y., and Ngan, A. H. W., 2009, “Deformation of Anodic Aluminum Oxide Nano-Honeycombs During Nanoindentation,” Acta Mater., 57(9), pp. 2710–2720. [CrossRef]
Wang, J., Evans, A. G., Dharmasena, K., and Wadley, H. N. G., 2003, “On the Performance of Truss Panels With Kagomé Cores,” Int. J. Solids Struct., 40(25), pp. 6981–6988. [CrossRef]
Wadley, H. N. G., Fleck, N., and Evans, A. G., 2003, “Fabrication and Structural Performance of Periodic Cellular Metal Sandwich Structures,” Compos. Sci. Technol., 63(16), pp. 2331–2343. [CrossRef]
Chiras, S., Mumm, D. R., Evans, A. G., Wicks, N., Hutchinson, J. W., Dharmasena, K., Wadley, H. N. G., and Fichter, S., 2002, “The Structural Performance of Near-Optimized Truss Core Panels,” Int. J. Solids Struct., 39(15), pp. 4093–4115. [CrossRef]
Hodge, A. M., Biener, J., Hayes, J. R., Bythrow, P. M., Volkert, C. A., and Hamza, A. V., 2007, “Scaling Equation for Yield Strength of Nanoporous Open-Cell Foams,” Acta Mater., 55(4), pp. 1343–1349. [CrossRef]
Hutchinson, R. G., and Fleck, N. A., 2006, “The Structural Performance of the Periodic Truss,” J. Mech. Phys. Solids, 54(4), pp. 756–782. [CrossRef]
Deshpande, V. S., Ashby, M. F., and Fleck, N. A., 2001, “Foam Topology: Bending Versus Stretching Dominated Architectures,” Acta Mater., 49(6), pp. 1035–1040. [CrossRef]
Jennings, A. T., Burek, M. J., and Greer, J. R., 2010, “Microstructure Versus Size: Mechanical Properties of Electroplated Single Crystalline Cu Nanopillars,” Phys. Rev. Lett., 104(13), p. 135503. [CrossRef] [PubMed]
Greer, J. R., and De Hosson, J. T. M., 2011, “Plasticity in Small-Sized Metallic Systems: Intrinsic Versus Extrinsic Size Effect,” Prog. Mater. Sci., 56(6), pp. 654–724. [CrossRef]
Greer, J. R., and Nix, W. D., 2005, “Size Dependence of Mechanical Properties of Gold at the Sub-Micron Scale,” Appl. Phys. A, 80(8), pp. 1625–1629. [CrossRef]
Greer, J. R., Oliver, W. C., and Nix, W. D., 2005, “Size Dependence of Mechanical Properties of Gold at the Micron Scale in the Absence of Strain Gradients,” Acta Mater., 53(6), pp. 1821–1830. [CrossRef]
Dou, R., and Derby, B., 2009, “A Universal Scaling Law for the Strength of Metal Micropillars and Nanowires,” Scr. Mater., 61(5), pp. 524–527. [CrossRef]
Greer, J. R., Jang, D., and Gu, X. W., 2012, “Exploring Deformation Mechanisms in Nanostructured Materials,” JOM, 64(10), pp. 1241–1252. [CrossRef]
Jang, D., and Greer, J. R., 2011, “Size-Induced Weakening and Grain Boundary-Assisted Deformation in 60 nm Grained Ni Nanopillars,” Scr. Mater., 64(1), pp. 77–80. [CrossRef]
Gu, X. W., Loynachan, C. N., Wu, Z., Zhang, Y.-W., Srolovitz, D. J., and Greer, J. R., 2012, “Size-Dependent Deformation of Nanocrystalline Pt Nanopillars,” Nano Lett., 12(12), pp. 6385–6392. [CrossRef] [PubMed]
Yang, B., Motz, C., Rester, M., and Dehm, G., 2012, “Yield Stress Influenced by the Ratio of Wire Diameter to Grain Size—A Competition Between the Effects of Specimen Microstructure and Dimension in Micro-Sized Polycrystalline Copper Wires,” Philos. Mag., 92(25–27), pp. 3243–3256. [CrossRef]
Rys, J., Valdevit, L., Schaedler, T. A., Jacobsen, A. J., Carter, W. B., and Greer, J. R., 2014, “Fabrication and Deformation of Metallic Glass Micro-Lattices,” Adv. Eng. Mater., 16(7), pp. 889–896. [CrossRef]
Chen, D. Z., Jang, D., Guan, K. M., An, Q., Goddard, W. A., and Greer, J. R., 2013, “Nanometallic Glasses: Size Reduction Brings Ductility, Surface State Drives Its Extent,” Nano Lett., 13(9), pp. 4462–4468. [CrossRef] [PubMed]
Chen, C. Q., Pei, Y. T., and De Hosson, J. T. M., 2010, “Effects of Size on the Mechanical Response of Metallic Glasses Investigated Through In Situ TEM Bending and Compression Experiments,” Acta Mater., 58(1), pp. 189–200. [CrossRef]
Volkert, C. A., Donohue, A., and Spaepen, F., 2008, “Effect of Sample Size on Deformation in Amorphous Metals,” J. Appl. Phys., 103(8), p. 083539. [CrossRef]
Valdevit, L., Jacobsen, A. J., Greer, J. R., and Carter, W. B., 2011, “Protocols for the Optimal Design of Multi-Functional Cellular Structures: From Hypersonics to Micro-Architected Materials,” J. Am. Ceram. Soc., 94(S1), pp. s15–s34. [CrossRef]
Lian, J., Jang, D., Valdevit, L., Schaedler, T. A., Jacobsen, A. J., Carter, W. B., and Greer, J. R., 2011, “Catastrophic Versus Gradual Collapse of Thin-Walled Nanocrystalline Ni,” Nano Lett., 11(10), pp. 4118–4125. [CrossRef] [PubMed]
Maloney, K. J., Roper, C. S., Jacobsen, A. J., Carter, W. B., Valdevit, L., and Schaedler, T. A., 2013, “Microlattices as Architected Thin Films: Analysis of Mechanical Properties and High Strain Elastic Recovery,” APL Mater., 1(2), p. 022106. [CrossRef]
Jacobsen, A. J., Barvosa-Carter, W., and Nutt, S., 2007, “Micro-Scale Truss Structures Formed From Self-Propagating Photopolymer Waveguides,” Adv. Mater., 19(22), pp. 3892–3896. [CrossRef]
Jacobsen, A. J., Barvosa-Carter, W., and Nutt, S., 2008, “Micro-Scale Truss Structures With Three-Fold and Six-Fold Symmetry Formed From Self-Propagating Polymer Waveguides,” Acta Mater., 56(11), pp. 2540–2548. [CrossRef]
Meza, L. R., and Greer, J. R., 2014, “Mechanical Characterization of Hollow Ceramic Nanolattices,” J. Mater. Sci., 49(6), pp. 2496–2508. [CrossRef]
Dietiker, M., Buzzi, S., Pigozzi, G., Löffler, J. F., and Spolenak, R., 2011, “Deformation Behavior of Gold Nano-Pillars Prepared by Nanoimprinting and Focused Ion-Beam Milling,” Acta Mater., 59(5), pp. 2180–2192. [CrossRef]
Volkert, C. A., and Lilleodden, E. T., 2006, “Size Effects in the Deformation of Sub-Micron Au Columns,” Philos. Mag., 86(33–35), pp. 5567–5579. [CrossRef]
Oh, S. H., Legros, M., Kiener, D., and Dehm, G., 2009, “In Situ Observation of Dislocation Nucleation and Escape in a Submicrometre Aluminium Single Crystal,” Nat. Mater., 8(2), pp. 95–100. [CrossRef] [PubMed]
Gu, X. W., and Greer, J. R., 2015, “Ultra-Strong Architected Cu Meso-Lattices,” Extreme Mech. Lett., 2, pp. 7–14. [CrossRef]
Fischer, J., and Wegener, M., 2013, “Three-Dimensional Optical Laser Lithography Beyond the Diffraction Limit,” Laser Photonics Rev., 7(1), pp. 22–44. [CrossRef]
Sun, H., and Kawata, S., 2004, “Two-Photon Photopolymerization and 3D Lithographic Microfabrication,” NMR, 3D Analysis, Photopolymerization (Advances in Polymer Science, Vol. 170), Springer-Verlag, Berlin, pp. 169–274.
Xiong, W., Zhou, Y. S., He, X. N., Gao, Y., Mahjouri-Samani, M., Jiang, L., Baldacchini, T., and Lu, Y. F., 2012, “Simultaneous Additive and Subtractive Three-Dimensional Nanofabrication Using Integrated Two-Photon Polymerization and Multiphoton Ablation,” Light: Sci. Appl., 1(4), p. e6. [CrossRef]
LaFratta, C. N., Fourkas, J. T., Baldacchini, T., and Farrer, R. A., 2007, “Multiphoton Fabrication,” Angew. Chem., Int. Ed. Engl., 46(33), pp. 6238–6258. [CrossRef]
Jeon, S., Malyarchuk, V., Rogers, J. A., and Wiederrecht, G. P., 2006, “Fabricating Three-Dimensional Nanostructures Using Two Photon Lithography in a Single Exposure Step,” Opt. Express, 14(6), pp. 2300–2308. [CrossRef] [PubMed]
Sun, H.-B., Matsuo, S., and Misawa, H., 1999, “Three-Dimensional Photonic Crystal Structures Achieved With Two-Photon-Absorption Photopolymerization of Resin,” Appl. Phys. Lett., 74(6), pp. 786–788. [CrossRef]
Tétreault, N., von Freymann, G., Deubel, M., Hermatschweiler, M., Pérez-Willard, F., John, S., Wegener, M., and Ozin, G. A., 2006, “New Route to Three-Dimensional Photonic Bandgap Materials: Silicon Double Inversion of Polymer Templates,” Adv. Mater., 18(4), pp. 457–460. [CrossRef]
Montemayor, L. C., Meza, L. R., and Greer, J. R., 2014, “Design and Fabrication of Hollow Rigid Nanolattices Via Two-Photon Lithography,” Adv. Eng. Mater., 16(2), pp. 184–189. [CrossRef]
Thornton, J. A., 1975, “Influence of Substrate Temperature and Deposition Rate on Structure of Thick Sputtered Cu Coatings,” J. Vac. Sci. Technol., 12(4), pp. 830–835. [CrossRef]
Thornton, J. A., 1986, “The Microstructure of Sputter-Deposited Coatings,” J. Vac. Sci. Technol., A, 4(6), pp. 3059–3065. [CrossRef]
Thornton, J. A., 1974, “Influence of Apparatus Geometry and Deposition Conditions on the Structure and Topography of Thick Sputtered Coatings,” J. Vac. Sci. Technol., 11(4), pp. 666–670. [CrossRef]
Valdevit, L., Dec. 2013, private communication.
Oliver, W., and Pharr, G., 1992, “An Improved Technique for Determining Hardness and Elastic Modulus Using Load and Displacement Sensing Indentation Experiments,” J. Mater. Res., 7(6), pp. 1564–1583. [CrossRef]
Thompson, C. V., 2000, “Structure Evolution During Processing of Polycrystalline Films,” Annu. Rev. Mater. Sci., 30, pp. 159–190. [CrossRef]


Grahic Jump Location
Fig. 3

Representative images of the Au coating in a 60 deg nanolattice with a wall thickness of ∼661 nm. In the center region, the nanolattice walls are conformal; however, the coating is not conformal near the edges of the lattice as a result of the anisotropy of the sputtering process.

Grahic Jump Location
Fig. 2

(a) Schematic of relevant geometric parameters on a nanolattice unit cell and (b) TEM image showing columnar grain structure of tubes with grain size on the order of 50 nm (TEM courtesy of Z. Aitken, scale bar 100 nm)

Grahic Jump Location
Fig. 1

Hierarchically structured materials combine structural and material size effects to enhance material properties and provide opportunities to create new materials that outperform current low-density materials. Material properties chart generated using CES SELECTOR (image courtesy of S. Das). (Figures reprinted with permission from Greer and De Hosson [20], Gu et al. [26], and Montemayor et al. [49]. Copyright 2011 by Elsevier Ltd. and 2012 by American Chemical Society, respectively.)

Grahic Jump Location
Fig. 4

SEM image of octahedron nanolattices with lattice angles from 30 deg to 60 deg, as well as representative stress–strain curve for each sample with an open circle showing the 0.2% yield stress of the structure. For the 30 deg lattice, it should be noted that the error bars are included but are small enough to be obscured by the data point itself (scale bar denotes 30 μm).

Grahic Jump Location
Fig. 5

Calculated yield stress and modulus values for lattices with angles ranging from 30 deg to 60 deg. The error bars were calculated by using the standard deviation of the data for yield stress and modulus (note: t = 352±87 nm for all samples).

Grahic Jump Location
Fig. 6

SEM image of 45 deg octahedron nanolattices with t ranging from 200 to 635 nm, as well as representative stress–strain curve for each sample with an open circle showing the 0.2% yield stress of the structure (scale bar denotes 20 μm)

Grahic Jump Location
Fig. 7

Calculated yield stress for both 45 deg and 60 deg octahedron nanolattices. The yield strength increases as (t/d) increases due to the material size effect.

Grahic Jump Location
Fig. 8

(a) Modulus versus sine of lattice angle according to Eq. (4) and (b) yield stress versus sine of lattice angle according to Eq. (5)

Grahic Jump Location
Fig. 9

TEM bright field image showing pores between grains as viewed through a section of a nanolattice wall, where the wall thickness is ∼200 nm

Grahic Jump Location
Fig. 10

(a) Ion channeling (sample at 52 deg tilt) and (b) TEM images of a ∼2 μm thin n-Au film showing columnar grain structure with multiple grains spanning the film thickness



Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In